Application of hydrophobic phthalocyanine as heterogeneous catalyst in oxidizing phenol wastewater by hydrogen peroxide

ABSTRACT

Disclosed is an application of a hydrophobic phthalocyanine as a heterogeneous catalyst in oxidizing phenol wastewater by hydrogen peroxide. A hydrophobic silane is decorated on a bacterial cellulose-metal phthalocyanine heterogeneous catalyst to obtain a hydrophobic phthalocyanine heterogeneous catalyst; during the catalytic degradation of phenols, the obtained catalyst is capable of adjusting a concentration of hydrogen peroxide oxidant around the catalyst. A preparation method of the hydrophobic phthalocyanine comprises: 1. preparing a mixed solution of a bacterial cellulose medium containing metal phthalocyanine; 2. adding acetic acid bacterium into the mixed solution obtained in step 1 for biological culture; 3. heating the product obtained in step 2, and taking out a solid for cleaning and drying; 4. preparing a hydrophobic silane solution; and 5. immersing the product obtained in step 3 into the solution obtained in step 4, and taking out a solid after reaction for cleaning and drying.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims foreign priority of Chinese Patent Application No. 202210156583.1, filed on Feb. 21, 2022 in the China National Intellectual Property Administration, the disclosures of all of which are hereby incorporated by reference.

TECHNICAL FIELD

The present invention belongs to the technical field of organic wastewater treatment; and particularly relates to an application of a hydrophobic phthalocyanine as a heterogeneous catalyst in oxidizing phenol wastewater by hydrogen peroxide and a preparation method of the hydrophobic phthalocyanine.

BACKGROUND

Metal phthalocyanine compounds are functional micromolecules with excellent properties, and a series of metal phthalocyanine derivatives with special physical and chemical properties can be obtained by changing the central metal atom and outer ring substituents thereof. Due to excellent chemical, optical and electrical properties, the metal phthalocyanine compounds may be applied to optical sensing materials, nonlinear optical materials, solar cell materials, fuel cells and other different fields. In particular, the structure of the metal phthalocyanine is highly similar to that of metalloporphyrin, the active center of active molecules such as chlorophyll and heme in nature. Inspired by this, researchers tried to apply the metal phthalocyanine to different catalytic reactions, and achieved remarkable achievements. In practice, in order to reuse the metal phthalocyanine, researchers often fix the metal phthalocyanine on solid carrier materials to prepare heterogeneous metal phthalocyanine catalysts. This technology can not only separate the metal phthalocyanine from the reaction system conveniently, but also reduce the problem of low catalytic activity caused by the formation of low-activity aggregates between phthalocyanine molecules, and avoid the secondary pollution caused by the phthalocyanine molecules entering the environment at the same time. The selection of suitable solid-phase carrier and preparation of heterogeneous metal phthalocyanine catalytic materials by a proper immobilization method have become research hotspots in the field of preparation and catalytic applications of metal phthalocyanine materials.

The application of the metal phthalocyanine in the treatment of organic pollutants and the catalytic oxidation and degradation of the organic pollutants with the help of oxidants (such as hydrogen peroxide (H₂O₂)) is one of the key concerns in the field of environmental purification. The basic catalytic degradation mechanism of the organic pollutants by the catalytic system of metal phthalocyanine+H₂O₂ is as follows: the metal phthalocyanine and H₂O₂ firstly form a metal phthalocyanine-OOH intermediate which would be cracked to form active species such as high valence metal=O and hydroxyl radical, and then the formed active species attack the organic pollutant molecules, finally achieving the object of catalytic oxidation and degradation. In actual reaction, in addition to forming the active species, H₂O₂ may also be decomposed into oxygen and water under the action of the metal phthalocyanine-OOH intermediate. The existence of this side reaction reduces the generation efficiency of the active species, and meanwhile, the obviously low utilization of H₂O₂ requires a much higher amount of H₂O₂ needed than that of a theoretical value in industrial applications. By constructing a suitable reaction micro-environment, the catalytic degradation efficiency of the catalyst for the organic pollutants can be effectively improved by adjusting the concentration of H₂O₂ around the metal phthalocyanine catalyst reasonably to reduce the possibility of side reaction with excess H₂O₂ after forming the metal phthalocyanine-OOH intermediate and increase the formation of the active species.

Based on the above analysis, it is of obvious application values in the fields of both catalysis and organic wastewater treatment by selecting a suitable metal phthalocyanine solid carrier and using a suitable immobilization method to obtain the heterogeneous metal phthalocyanine catalytic materials, and constructing a suitable reaction micro-environment for the heterogeneous metal phthalocyanine catalytic materials, so that H₂O₂ can be effectively utilized to generate the active species while using the heterogeneous metal phthalocyanine catalytic materials to treat industrial organic wastewater such as phenols, and the catalytic reaction efficiency of the catalyst can be improved.

SUMMARY

The object of the present invention is to provide a simple, efficient and green bacterial cellulose-metal phthalocyanine heterogeneous catalyst for oxidative degradation of phenolic industrial wastewater and a preparation method thereof, and then decorate a hydrophobic silane on the bacterial cellulose-metal phthalocyanine heterogeneous catalyst to obtain the hydrophobic phthalocyanine heterogeneous catalyst. With H₂O₂ as an oxidant, the hydrophobic phthalocyanine heterogeneous catalyst can efficiently catalyze the oxidative degradation of phenols. During the catalytic degradation of phenols, the obtained hydrophobic phthalocyanine heterogeneous catalyst can adjust a concentration of the hydrogen peroxide oxidant around the catalyst, limit side reactions in the catalytic process, and achieve the object of significantly improving the catalytic degradation efficiency. According to the present invention, the bacterial cellulose is selected as the solid carrier and reducing agent of the metal phthalocyanine, which realizes the immobilization of metal phthalocyanine at the same time of reduction; the possibility of side reactions in the catalytic reaction process is skillfully reduced through the hydrophobic silane, thus significantly improving the catalytic degradation efficiency of the heterogeneous catalysts on organic pollutants.

In a first aspect, the present invention provides an application of oxidizing phenol wastewater by hydrogen peroxide with a hydrophobic phthalocyanine as a heterogeneous catalyst, wherein the hydrophobic phthalocyanine is obtained by decorating a hydrophobic group on a bacterial cellulose-metal phthalocyanine with a silane coupling agent; the bacterial cellulose-metal phthalocyanine is obtained by mixing a metal phthalocyanine into a bacterial cellulose medium, biologically culturing with an acetic acid bacterium, and then heating and reducing the mixture; and the metal phthalocyanine is nitro-sulfonic metal phthalocyanine (with a structure referring to formula 1).

-   -   Formula 1: structural formula of the nitro-sulfonic metal         phthalocyanine, wherein a central metal M is one of iron (III)         or cobalt (II)

In a second aspect, the present invention provides a hydrophobic phthalocyanine for catalytic degradation of phenols, wherein the hydrophobic phthalocyanine is obtained by modifying a hydrophobic group on a bacterial cellulose-metal phthalocyanine with a silane coupling agent; the bacterial cellulose-metal phthalocyanine is obtained by mixing a metal phthalocyanine into a bacterial cellulose medium, culturing the mixture with an acetic acid bacterium, and then heating and reducing the mixture; and the metal phthalocyanine is nitro-sulfonic metal phthalocyanine.

Preferably, the process of decorating the hydrophobic group on the bacterial cellulose-metal phthalocyanine is: adding the bacterial cellulose-metal phthalocyanine in a silane coupling agent solution for treatment.

In a third aspect, the present invention provides a preparation method of the fore-mentioned hydrophobic phthalocyanine heterogeneous catalyst for catalytic degradation of phenols, wherein the preparation method comprises the following steps of:

step 1. preparing a mixed solution of a bacterial cellulose medium containing metal phthalocyanine;

step 2. adding an acetic acid bacterium into the mixed solution obtained in step 1 for biological culture;

step 3. heating the product obtained in step 2, and taking out a solid for cleaning and drying;

step 4. preparing a hydrophobic silane coupling agent solution; and

step 5. immersing the product obtained in step 3 into the solution obtained in step 4, and taking out a solid after reaction for cleaning and drying to obtain the hydrophobic phthalocyanine.

Preferably, in step 1, the bacterial cellulose medium consists of a glucose, a peptone, a yeast extract and a disodium hydrogen phosphate, wherein concentrations of the glucose, the peptone, the yeast extract and the disodium hydrogen phosphate are 2% to 10%, 0.2% to 1%, 0.2% to 1% and 0.02% to 0.1% respectively; and a concentration of the nitro-sulfonic metal phthalocyanine in the mixed solution is 0.5% to 5%.

Preferably, in step 2, the acetic acid bacterium is one of Gluconacetobacter intermedius, Acetobacter xylinum or Acetobacter Hansenii. Conditions for the biological culture are as follows: a culture temperature ranges from 20° C. to 35° C., and a culture time ranges from 3 days to 10 days.

Preferably, in step 3, the heating is carried out in a temperature range of 80° C. to 99° C. and the reaction time ranges from 12 hours to 72 hours; the cleaning process comprises sequentially cleaning with a hydrochloric acid solution, a sodium hydroxide solution and ultrapure water; a concentration of the hydrochloric acid solution ranges from 0.10 mol/L to 1 mol/L, and a concentration of the sodium hydroxide solution ranges from 0.10 mol/L to 1 mol/L.

Preferably, in step 5, the reaction conditions are as follows: a reaction temperature is 25° C., and a reaction time is 24 hours; and the cleaning process comprises sequentially cleaning with absolute ethyl alcohol and ultrapure water.

Preferably, in step 4, the silane coupling agent is one of trimethoxymethylsilane (CAS No.: 1185-55-3), ethyltrimethoxysilane (CAS No.: 5314-55-6), trimethoxy(propyl)silane (CAS No.: 1067-25-0), trimethoxyphenylsilane (CAS No.: 2996-92-1) or hexadecyltrimethoxysilane (CAS No.: 16415-12-6), the solvent used is toluene, and a concentration range of the hydrophobic silane in the solution is 1 g/L to 50 g/L.

In a fourth aspect, the present invention provides a method for treating phenolic wastewater, comprising the process as follows: adding the hydrophobic phthalocyanine as a catalyst, and H₂O₂ as an oxidant into the treated wastewater.

Compared with the prior art, the present invention has the following beneficial effects.

1. In the present invention, the bacterial cellulose-metal phthalocyanine heterogeneous catalyst is modified with the hydrophobic group by the silane coupling agent, and the prepared hydrophobic phthalocyanine heterogeneous catalyst may be used for efficient catalytic degradation of phenolic organic pollutants. Due to the existence of the hydrophobic group, the process of hydrophilic hydrogen peroxide approaching the heterogeneous catalyst is hindered, which makes the concentration of the oxidant around the heterogeneous catalyst reasonably adjusted in the process of phenol catalytic degradation. The decreased side reactions of excess H₂O₂ could reduce the likelihood of low utilization and effectively improve the catalytic degradation efficiency of the heterogeneous catalyst on the organic pollutants by increasing the formation of active species. Meanwhile, the hydrophobic phthalocyanine heterogeneous catalyst obtained by the present invention has the advantage of being reusable.

2. The present invention provides a preparation method of a phthalocyanine heterogeneous catalyst. In this method, the bacterial cellulose is selected as the solid carrier and reducing agent of the metal phthalocyanine, which realizes immobilization of the metal phthalocyanine by forming the hydrogen bond between the bacterial cellulose and the amino-sulfonic metal phthalocyanine while reducing the nitro-sulfonic metal phthalocyanine into the amino-sulfonic metal phthalocyanine. Compared with other preparation methods, the preparation method provided by the present invention omits the process of additionally using a chemical reducing agent to convert the nitro-sulfonic metal phthalocyanine into the amino-sulfonic metal phthalocyanine in the prior art, and enables the amino-sulfonic metal phthalocyanine to be fully and uniformly loaded on the bacterial cellulose, and has the advantages of simple preparation process, green preparation process, economy, high efficiency and the like.

3. According to the present invention, the metal phthalocyanine is added into the bacterial cellulose medium and then loads on the bacterial cellulose while the acetic acid bacterium produce the bacterial cellulose. In this process, since the bacterial cellulose continues to grow, the position of the metal phthalocyanine originally loaded on the surface of the bacterial cellulose is changed to the interior of the bacterial cellulose. However, the surface of the grown bacterial cellulose continues to be loaded with the metal phthalocyanine, so that the surface and the interior of the bacterial cellulose are both uniformly loaded with the metal phthalocyanine. Therefore, a large number of catalytic active sites are formed in the interior of the bacterial cellulose due to the ultra-high specific surface area and three-dimensional network structure of the bacterial cellulose, thus significantly improving the catalytic activity of the prepared catalyst.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a curve showing a change of a phenol solution concentration with a reaction time under the action of a hydrophobic phthalocyanine heterogeneous catalyst provided by the present invention; and

FIG. 2 is a diagram showing a change of a cyclic catalytic degradation performance of the hydrophobic phthalocyanine heterogeneous catalyst provided by the present invention to the phenol solution.

DETAILED DESCRIPTION

The technical solutions in the present invention will be described clearly and completely below. Apparently, the described embodiments are merely some but not all of the embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skills in the art without going through any creative work shall fall within the protection scope of the present invention.

Embodiment 1

A preparation method of a hydrophobic phthalocyanine heterogeneous catalyst for catalytic degradation of phenols, comprised the following steps.

(1) 12.00 g of glucose, 1.25 g of peptone, 1.25 g of yeast extract and 0.10 g of disodium hydrogen phosphate were dissolved in 100 mL of ultrapure water, and then added with 2.50 g of nitro-sulfonic iron phthalocyanine to prepare a mixed solution of a bacterial cellulose medium containing metal phthalocyanine.

(2) An acetic acid bacterium was added into the mixed solution obtained in step (1) and cultured for 7 days at 30° C.

(3) The product obtained in step (2) was heated to 90° C. for 24 hours, and the nitro-sulfonic iron phthalocyanine was reduced to amino-sulfonic iron phthalocyanine with the reaction of bacterial cellulose. The metal phthalocyanine was immobilized on the bacterial cellulose by forming a hydrogen bond between the bacterial cellulose and the amino-sulfonic iron phthalocyanine. The solid product was taken out, and cleaned with 0.20 mol/L hydrochloric acid, 0.20 mol/L sodium hydroxide and ultrapure water in turn, and then dried to obtain the bacterial cellulose-metal phthalocyanine heterogeneous catalyst.

(4) 0.50 g of hexadecyltrimethoxysilane, served as a silane coupling agent, was dissolved in 50 mL of toluene to prepare a hydrophobic silane solution.

(5) The product obtained in step (3) was immersed in the solution obtained in step (4) and reacted for 24 hours at 25° C. The solid product was taken out, and cleaned with absolute ethyl alcohol and ultrapure water in turn, and then dried to obtain the hydrophobic phthalocyanine heterogeneous catalyst. A content of the metal phthalocyanine in the obtained hydrophobic phthalocyanine heterogeneous catalyst was 118 μmol/g.

Comparative Example 1

Compared with Embodiment 1, step (3) was not carried out in this comparative example, and other steps and conditions were the same as that in Embodiment 1.

A content of the metal phthalocyanine in the finally obtained hydrophobic phthalocyanine heterogeneous catalyst was 36 μmol/g. By comparing the data of Embodiment 1 and Comparative Example 1, it could be seen that less nitro-sulfonic iron phthalocyanine was immobilized on the bacterial cellulose. After the bacterial cellulose reduced the nitro-sulfonic iron phthalocyanine into the amino-sulfonic iron phthalocyanine, hydrogen bond interaction was formed between the hydroxyl group on the bacterial cellulose and the amino group on the amino-sulfonic iron phthalocyanine, which realized efficient immobilization of the amino-sulfonic iron phthalocyanine on the bacterial cellulose, thus obtaining the bacterial cellulose-metal phthalocyanine heterogeneous catalyst.

Comparative Example 2

Compared with Embodiment 1, step (4) and step (5) were not carried out in this comparative example, and other steps and conditions were the same as that in Embodiment 1.

A content of the metal phthalocyanine in the finally obtained bacterial cellulose-metal phthalocyanine heterogeneous catalyst was 118 μmol/g. By comparing the data of Embodiment 1, Comparative Example 1 and Comparative Example 2, it could be seen that the hydrophobizing treatment step did not affect the content of the metal phthalocyanine on the heterogeneous catalyst.

Embodiment 2

The hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 1 was subjected to a catalytic oxidation and degradation performance test, and organic pollutants degraded in the test were phenol organic pollutants. The specific test process was as follows.

1.50 mg of the hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 1 were applied to the catalytic oxidation and degradation of phenol organic pollutants. The specific experimental conditions were as follows: an initial concentration of a phenol solution was 1×10⁻³ mol/L, a volume of the phenol solution was 20 mL, a pH value of the phenol solution was adjusted to 3, a concentration of a H₂O₂ oxidant was 50 mmol/L, and a reaction temperature was 50° C. After reaction for 40 minutes, the concentration of the phenol solution decreased by 89.29%. After reaction for 60 minutes, the concentration of the phenol solution decreased by 97.86%. The specific experimental results were shown in FIG. 1 , which showed that the obtained hydrophobic phthalocyanine heterogeneous catalyst had excellent catalytic oxidation and degradation performance on the phenol organic pollutants.

In order to investigate the reusability of the obtained hydrophobic phthalocyanine heterogeneous catalyst, the above-mentioned hydrophobic phthalocyanine heterogeneous catalyst was taken out of the reaction solution, washed with ultrapure water and used again for catalytic oxidation and degradation of the phenol solution under the same experimental conditions. After repeated use for 10 times, the hydrophobic phthalocyanine heterogeneous catalyst could still reduce the concentration of the phenol solution by 95.56% under the same experimental conditions. The specific experimental results were shown in FIG. 2 , which showed that the hydrophobic phthalocyanine heterogeneous catalyst had excellent reusability.

Comparative Example 3

1.50 mg of the bacterial cellulose-metal phthalocyanine heterogeneous catalyst obtained in Comparative Example 2 were applied to catalytic oxidation and degradation of phenol organic pollutants. Other experimental conditions were the same as those described in Embodiment 2. After reaction for 40 minutes, the concentration of the phenol solution decreased by 68.27%. After reaction for 60 minutes, the concentration of the phenol solution decreased by 80.66%. It could be seen from Embodiment 2 and Comparative Example 3 that decorating the hydrophobic silane on the bacterial cellulose-metal phthalocyanine heterogeneous catalyst was beneficial to improve the catalytic efficiency of the catalyst.

Embodiment 3

The hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 1 was subjected to a catalytic oxidation and degradation performance test, and organic pollutants degraded in the test were 4-chlorophenol organic pollutants. The specific test process was as follows.

1.50 mg of the hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 1 were applied to the catalytic oxidation and degradation of 4-chlorophenol organic pollutants. The specific experimental conditions were as follows: an initial concentration of a 4-chlorophenol solution was 1×10⁻³ mol/L, a volume of the 4-chlorophenol solution was 20 mL, a pH value of the 4-chlorophenol solution was adjusted to 3, a concentration of a H₂O₂ oxidant was 50 mmol/L, and a reaction temperature was 50° C. After reaction for 50 minutes, the concentration of the 4-chlorophenol solution decreased by 92.35%, which showed that the obtained hydrophobic phthalocyanine heterogeneous catalyst also had excellent catalytic oxidation and degradation performance on the 4-chlorophenol organic pollutants.

Comparative Example 4

1.50 mg of the bacterial cellulose-metal phthalocyanine heterogeneous catalyst obtained in Comparative Example 2 were applied to catalytic oxidation and degradation of 4-chlorophenol organic pollutants under the same experimental conditions in Embodiment 3. After reaction for 50 minutes, the concentration of the 4-chlorophenol solution decreased by 62.81%. It could be seen from the data of Embodiment 4 and Comparative Example 3 that modification of the bacterial cellulose-metal phthalocyanine heterogeneous catalyst with the hydrophobic silane was beneficial to improve the catalytic efficiency of the catalyst.

Embodiment 4

A preparation method of a hydrophobic phthalocyanine heterogeneous catalyst for catalytic degradation of phenols, comprised the following steps.

(1) 12.00 g of glucose, 1.25 g of peptone, 1.25 g of yeast extract and 0.10 g of disodium hydrogen phosphate were dissolved in 100 mL of ultrapure water, and then added with 5.00 g of nitro-sulfonic iron phthalocyanine to prepare a mixed solution of a bacterial cellulose medium containing metal phthalocyanine.

(2) An acetic acid bacterium was added into the mixed solution obtained in step (1) and cultured for 7 days at 30° C.

(3) The product obtained in step (2) was heated to 95° C. for 60 hours, and the nitro-sulfonic iron phthalocyanine was reduced to amino-sulfonic iron phthalocyanine with the reaction of bacterial cellulose. The metal phthalocyanine was immobilized on the bacterial cellulose by forming a hydrogen bond between the bacterial cellulose and the amino-sulfonic metal phthalocyanine. The solid product was taken out, and cleaned with 0.20 mol/L hydrochloric acid, 0.20 mol/L sodium hydroxide and ultrapure water in turn, and then dried to obtain the bacterial cellulose-metal phthalocyanine heterogeneous catalyst.

(4) 1.50 g of trimethoxy(propyl)silane were dissolved in 50 mL of toluene to prepare a hydrophobic silane solution.

(5) The product obtained in step (3) was immersed in the solution obtained in step (4) and reacted for 24 hours at 25° C. The solid product was taken out, and cleaned with absolute ethyl alcohol and ultrapure water in turn, and then dried to obtain the hydrophobic phthalocyanine heterogeneous catalyst. A content of the metal phthalocyanine in the obtained hydrophobic phthalocyanine heterogeneous catalyst was 228 μmol/g.

Embodiment 5

The hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 4 was subjected to a catalytic oxidation and degradation performance test, and organic pollutants degraded in the test were phenol organic pollutants. The specific test process was as follows:

1.50 mg of the hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 4 were applied to the catalytic oxidation and degradation of phenol organic pollutants under the same experimental conditions in Embodiment 2. After reaction for 30 minutes, the concentration of the phenol solution decreased by 91.04%.

Embodiment 6

The hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 4 was subjected to a catalytic oxidation and degradation performance test, and organic pollutants degraded in the test were 4-chlorophenol organic pollutants. The specific test process was as follows:

1.50 mg of the hydrophobic phthalocyanine heterogeneous catalyst obtained in Embodiment 4 were applied to the catalytic oxidation and degradation of 4-chlorophenol organic pollutants under the same experimental conditions in Embodiment 4. After reaction for 35 minutes, the concentration of the phenol solution decreased by 92.87%.

The above are only the preferred embodiments of the present invention, so the scope of implementation of the present invention cannot be limited accordingly, that is, the equivalent changes and modifications made according to the patent scope of the present invention and the contents of the specification should still fall within the scope of the present invention. 

1. An application of a hydrophobic phthalocyanine as a heterogeneous catalyst in oxidizing phenol wastewater by hydrogen peroxide, wherein the hydrophobic phthalocyanine is obtained by decorating a hydrophobic group on a bacterial cellulose-metal phthalocyanine with a silane coupling agent; the bacterial cellulose-metal phthalocyanine is obtained by mixing a metal phthalocyanine into a bacterial cellulose medium, biologically culturing with an acetic acid bacterium, and then heating and reducing the mixture; and the metal phthalocyanine is nitro-sulfonic metal phthalocyanine.
 2. A hydrophobic phthalocyanine for catalytic degradation of phenols, wherein the hydrophobic phthalocyanine is obtained by decorating a hydrophobic group on a bacterial cellulose-metal phthalocyanine with a silane coupling agent; the bacterial cellulose-metal phthalocyanine is obtained by mixing a metal phthalocyanine into a bacterial cellulose medium, culturing the mixture with an acetic acid bacterium, and then heating and reducing the mixture; and the metal phthalocyanine is nitro-sulfonic metal phthalocyanine.
 3. The hydrophobic phthalocyanine for the catalytic degradation of phenols according to claim 2, wherein the process of decorating the hydrophobic group on the bacterial cellulose-metal phthalocyanine is: adding the bacterial cellulose-metal phthalocyanine in a silane coupling agent solution for treatment.
 4. A method for preparing the hydrophobic phthalocyanine for the catalytic degradation of phenols of claim 2, comprising the following steps of: step
 1. preparing a mixed solution of a bacterial cellulose medium containing metal phthalocyanine; step
 2. adding an acetic acid bacterium into the mixed solution obtained in step 1 for biological culture; step
 3. heating the product obtained in step 2, and taking out a solid for cleaning and drying; step
 4. preparing a hydrophobic silane coupling agent solution; and step
 5. immersing the product obtained in step 3 into the solution obtained in step 4, and taking out a solid after reaction for cleaning and drying to obtain the hydrophobic phthalocyanine.
 5. The method according to claim 4, wherein in step 1, the bacterial cellulose medium consists of a glucose, a peptone, a yeast extract and a disodium hydrogen phosphate, wherein concentrations of the glucose, the peptone, the yeast extract and the disodium hydrogen phosphate are 2% to 10%, 0.2% to 1%, 0.2% to 1% and 0.02% to 0.1% respectively; and a concentration of the nitro-sulfonic metal phthalocyanine in the mixed solution is 0.5% to 5%.
 6. The method according to claim 4, wherein in step 2, the acetic acid bacterium is one of Gluconacetobacter intermedius, Acetobacter xylinum or Acetobacter Hansenii; and conditions for the biological culture are as follows: a culture temperature ranges from 20° C. to 35° C., and a culture time ranges from 3 days to 10 days.
 7. The method according to claim 4, wherein in step 3, the heating is carried out in a temperature range of 80° C. to 99° C. and the reaction time ranges from 12 hours to 72 hours; the cleaning process comprises sequentially cleaning with a hydrochloric acid solution, a sodium hydroxide solution and ultrapure water; a concentration of the hydrochloric acid solution ranges from 0.10 mol/L to 1 mol/L, and a concentration of the sodium hydroxide solution ranges from 0.10 mol/L to 1 mol/L.
 8. The method according to claim 7, wherein in step 5, the reaction conditions are as follows: a reaction temperature is 25° C., and a reaction time is 24 hours; and the cleaning process comprises sequentially cleaning with absolute ethyl alcohol and ultrapure water.
 9. The method according to claim 4, wherein in step 4, the silane coupling agent is one of trimethoxymethylsilane, ethyltrimethoxysilane, trimethoxy(propyl)silane, trimethoxyphenylsilane or hexadecyltrimethoxysilane, the solvent used is toluene, and a concentration range of the hydrophobic silane in the solution is 1 g/L to 50 g/L.
 10. A method for treating phenolic wastewater, comprising the process as follows: adding the hydrophobic phthalocyanine of claim 2 as a catalyst, and H₂O₂ as an oxidant into the treated wastewater. 